Nickel Matrix Alloy Flux Coated Tungsten Carbide Welding Rods 1/8''-1/16''

Product Details:
Place of Origin: Zhuzhou,China
Brand Name: CHAOYU
Certification: ISO9001:2008
Model Number: 450mm length
Payment & Shipping Terms:
Minimum Order Quantity: 1 KG
Price: Negotiable
Packaging Details: Standard export carton
Delivery Time: 7-10 working days
Payment Terms: L/C, D/A, D/P, T/T, Western Union, MoneyGram
Supply Ability: 10 tons per month
Contact Now

Detail Information

Item Name: Flux Coated Tungsten Carbide Welding Rod Carbide Content: 60%
Carbide Size Inch: 1/8''-1/16'' Grit: Crushed Tungsten Carbide Grits
High Light:

tungsten carbide bar

,

carbide drill rod

Product Description

Nickel Matrix Alloy Flux Coated Tungsten Carbide Welding Rods​
 
Brief Introduction
 
1.tungsten carbide brazing rods they are made of by sintering tungsten carbide scrap and elastic
matrix alloy,
Outer layer of the special flux and coloring is marking scrap grade,the composition of sintering
tungsten carbide scrap is mainly CO and WC,The hardness is HRA 89~91,tire body matal is Ni and copper
alloy,strength can up to 690MPa, hardness HB
160.
 
Nickel Matrix Alloy Flux Coated Tungsten Carbide Welding Rods 1/8''-1/16''
 
 
Property
1.Carbide content: 65%,70%
2.Hardness Carbide
(HRA): ≥89.5
3.Matrix alloy melting range: 890-910°C
4.Composite rod size:
Length: 280mm,350mm,450 mm,450mm
Diamter: 12mm,12mm,16mm,22mm
 
carbide partical size  inch 
1 1/8" – 1/16"
2
3/16" – 1/8"
3
1/4" – 3/16"
4
5/16" – 1/4"
5
3/8" – 5/16"

 

 
Mass production pic 
 
The oxyacetylene butt, the operating process is as follows:
(1) clean up the workpiece, make the welding workpieces surface with metallic luster.
(2) the flat position of welding, therefore can use the appropriate clamping fixture for control of surfacing layer thickness, thick piece of available.
(3) with a neutral flame preheating, flame core not contact surface, the distance to 25 mm is advisable.
(4) carbide surfacing welding layer.With YD type electrode surfacing, the use of neutral flame (can be slightly carbonizing flame) tip is steady on the workpiece surface movement, the flame of the alloy electrode heating (be careful not to make flame cone tip contact alloy particles), tire body in the electrode alloy melt, carbide particles are also falling.Before the tire body of molten metal solidification, the particles arrange, can use left hand of the alloy electrode fingers, or another person holding a base electrode or pull rod on graphite rod in a quick stir particles, making them evenly aligned neatly.Surfacing layer thickness control according to the requirements of design.
(5) after the workpiece welding, where no ventilation, slow cooling, cannot quench, conditional usable asbestos blanket cover.
(6) the workpiece after cooling to room temperature, if necessary, grinding surface surfacing to required size and shape.
(7) clean up the workpiece, remove all splash, slag, etc.
 
Nickel Matrix Alloy Flux Coated Tungsten Carbide Welding Rods 1/8''-1/16''

 

Related products:

Tungsten carbide balls and seats 

Tungsten carbide buttons 

Tungsten carbide plates and strips 

Tungsten carbide rods 

Tungsten carbide rollers 

Tungsten carbide disc cutters 

Tungsten carbide blades

Tungsten carbide special parts

 

Contact

 

Nickel Matrix Alloy Flux Coated Tungsten Carbide Welding Rods 1/8''-1/16''

 
 

Get in touch with us

Enter Your Message

You Might Be Into These